拉伸断裂伸长率(延伸率)
ASTM D638/ISO 527
>50
%
弯曲模量(弯曲弹性率)
ASTM D790/ISO 178
2400
kg/cm²(MPa)[Lb/in2]
弯曲强度
ASTM D790/ISO 178
97
kg/cm²(MPa)[Lb/in2]
洛氏硬度
ASTM D785
IZOD 缺口冲击强度
1/4" 23℃
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
1/4" -30℃
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
1/8" 23℃
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
1/8" -30℃
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
Charpy冲击强度
23℃ (缺口)
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
-30℃(缺口)
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
23℃(无缺口)
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
-30℃(无缺口)
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
物性性能
比重(密度)
ASTM D792/ISO 1183
成型收缩率
ASTM D955
0.60-0.80
%
熔融指数(流动系数)
200℃/5kg
ASTM D1238/ISO 1133
g/10min
220℃/10kg
ASTM D1238/ISO 1133
g/10min
吸水率 23℃/24H
ASTM D570/ISO 62
0.30
%
热性能
热变形温度
退火
ASTM D648/ISO 75
℃(℉)
未退火
ASTM D648/ISO 75
137
℃(℉)
维卡软化点
ASTM D1525/ISO R306
146
℃(℉)
熔点
-
℃(℉)
燃烧性(率)
UL94
线性膨胀系数
ASTM D696/ISO 11359
0.000065
mm/mm.℃